A covered arc welding electrode includes a steel core wire and a flux which is applied to the outside periphery of said steel core wire. The welding electrode can form a superior crack-resisting weld zone even if fluctuating stresses are continually applied to a base metal while the base metal is welded. The flux includes 40 to 60% metal carbonate, 10 to 25% metal fluoride and 4 to 25 metal oxide by weight. The flux comprises 24 to 32% of the total weight of said electrode. The composition of the welding electrode includes 0.005 to 0.05% carbon, 0.1 to 1.1% silicon, 1.5 to 2.5% manganese, not more than 0.007% sulfur and not more than 0.25% nickel by weight and the manganese/sulfur ratio is more than or equal to 350 to 1. In addition, the welding electrode can include 0.01 to 0.10% rare earth metal by weight. In which case, the Mn content may be 1.0 to 2.5% by weight and the manganese/sulfur ratio may be more than or equal to 270 to 1. In addition, the composition of the welding electrode can include titanium and zirconium, the total content of which may be less than or equal to 1.2% the total weight of the electrode, and/or aluminum and magnesium, the total content of which may be less than or equal to 1.2% of the total weight of the electrode.
1. A covered arc welding electrode comprising:
a flux including 40 to 60% metal carbonate, 10 to 25% metal fluoride and 4 to 25% metal oxide by weight; and a steel core wire, onto the outer periphery of which said flux is applied so as to comprise 24 to 32% of the total weight of said electrode, said electrode as a whole being comprised of 0.005 to 0.05% carbon, 0.1 to 1.1% silicon, 1.5 to 2.5% manganese, not more than 0.007% sulfur and not more than 0.25% nickel by weight and in which the manganese/sulfur ratio is more than or equal to 350 to 1.
a flux including 40 to 60% metal carbonate, 10 to 25% metal fluoride and 4 to 25% metal oxide by weight; and a steel core wire, onto the outer periphery of which said flux is applied so as to comprise 24 to 32% of the total weight of said electrode, said electrode as a whole being comprised of 0.005 to 0.05% carbon, 0.1 to 1.1% silicon, 1.5 to 2.5% manganese, not more than 0.007% sulfur and not more than 0.25% nickel by weight and in which the manganese/sulfur ratio is more than or equal to 350 to 1.
2. A covered arc-welding electrode as set forth in claim 1, further comprising titanium and zirconium, the total content of which is less than or equal to 1.2% of the total weight of the electrode.
3. A covered arc-welding electrode as set forth in claim 2, further comprising aluminum and magnesium, the total content of which is less than or equal to 1.2% of the total weight of the electrode.
4. A covered arc-welding electrode as set forth in claim 1, further comprising aluminum and magnesium, the total content of which is less than or equal to 1.2% of the total weight of the electrode.
5. A covered arc-welding electrode comprising:
a flux including by weight 40 to 60% metal carbonate, 10 to 25% metal fluoride and 4 to 25% metal oxide; and a steel core wire, onto the outer periphery of which said flux is applied so as to comprise 24 to 32% of the total weight of said electrode;
said electrode as a whole being comprised of 0.005 to 0.05% carbon, 0.1 to 1.1% silicon, 1.0 to 2.5% manganese, not more than 0.007% sulfur, not more than 0.25% nickel and 0.01 to 0.10% rare earth metal by weight and in which the manganese/sulfur ratio is more than or equal to 270 to 1.
a flux including by weight 40 to 60% metal carbonate, 10 to 25% metal fluoride and 4 to 25% metal oxide; and a steel core wire, onto the outer periphery of which said flux is applied so as to comprise 24 to 32% of the total weight of said electrode;
said electrode as a whole being comprised of 0.005 to 0.05% carbon, 0.1 to 1.1% silicon, 1.0 to 2.5% manganese, not more than 0.007% sulfur, not more than 0.25% nickel and 0.01 to 0.10% rare earth metal by weight and in which the manganese/sulfur ratio is more than or equal to 270 to 1.
6. A covered arc-welding electrode as set forth in claim 5, further comprising titanium and zirconium, the total content of which is less than or equal to 1.2% of the total weight of the electrode.
7. A covered arc-welding electrode as set forth in claim 6, further comprising aluminum and magnesium, the total content of which is less than or equal to 1.2% of the total weight of the electrode.
8. A covered arc-welding electrode as set forth in claim 5, further comprising aluminum and magnesium, the total content of which is less than or equal to 1.2% of the total weight of the electrode.